Ferro vanadium muaj
(1) Vanadium pentoxide ntau lawm
Cov tshuaj muaj pes tsawg leeg ntawm vanadium ore yog: v{{{0}}.3%-1.4%, Fe txog 60%, TiO2 txog 14%. Vanadium-muaj hlau npua yog tau los ntawm kev txo cov vanadium ore nrog coke nyob rau hauv lub cub tawg (los yog hluav taws xob cub tawg). Nws muaj v0.4%-1.2%, si<0.5%, and Ti about 0.3%. The vanadium slag obtained by blowing the pig iron with oxygen in a top-blown oxygen converter (or ladle) contains V10%-15%, feo25%-45%, sio213%-20%, TiO2 about 10%, and cr2o31%-5.0%. The slag is mixed with metallic iron (semi-steel). After crushing and ball milling, the particle size is less than 0.1mm. The metallic iron is selected by air separator or magnetic separator and used as raw material for the production of Vanadium pentoxide. Vanadium exists in the spinel phase in vanadium slag. V2O3 should be oxidized to V2O5 by oxidation method, and then combined with Na2O to form water-soluble sodium vanadate. Use soda ash and Glauber's salt.
ferro vanadium hmoov
Ferro Vanadium Lump